City Glass Puddle

So today I cut a glass puddle shape and trapped my copper drawn samples inside. I used 3mm glass thickness which was good because it was relatively easy to cut and get the accurate shape for the puddles. When I was sanding down the glass I noticed it was chipping along the edges, I left this on there because maybe it would cause a rippled effect like in water I shall have to test this in the kiln. I am waiting for this to be fired.